新款塑料低溫脆化試驗機檢查電線電纜塑料外殼以及硫化橡膠在低溫測試時的脆化特性。  

The embrittlement of  plastic case of the wire and the embrittlement of vulcanized rubber during low  temperature test.

用戶可以選擇TS-BC直線性沖擊試驗方法或者TS-BT擺錘型沖擊試驗方法以滿足客戶對設備的不同需求。  

The user can choose the  TS-BC linear impact test method or TS-BT pendulum te impact test method to  meet the customer's different needs of the equipment.

試驗時將試樣固定于夾具上，然后將試樣浸泡坐在低溫介質中5分鐘，用2±0.2m/s的線速度沖擊試樣，后檢查試樣在溫度是否出現裂紋、裂縫、小孔、以及是否完分離成碎片。  

Test sample is fixed on  the fixture, then soaked samples sitting in low temperature medium in 5 minutes,  with 2 + 0.2 M / s line speed impact test specimens, the final inspection sample  in the lowest temperature whether cracks, cracks, holes, and whether separates  into pieces.

通過轉換卡盤托架底座可以連續的進行樣品測試，可以節省樣品放回原處時間，滿足很多樣品各自的測試標準。  

Through the conversion of  the chuck bracket base can be continuous sample test, can save the sample back  in place of time, meet a lot of samples of the respective test standard.  

新款塑料低溫脆化試驗機制冷方式 The  refrigeration mode of multifunctional plastic cryogenic embrittlement test  machine
采用二段式壓縮機快速降溫制冷，溫度可達-76℃(如需低于-76℃，可定制)。  

Two stage compressor  cooling refrigeration, the lowest temperature of up to -76 (for example, can be  customized for less than -76).

溫度可控性高，低溫槽中液體傳熱介質可啟用攪拌馬達，使溫度均勻性更佳。毎次可測試4組試樣， 旋轉定位夾具對每組試樣進行沖擊測試，檢査出現脆性破壞的溫度。  

The temperature can be  controlled and the heat transfer medium of the liquid in the cryogenic tank can  be used for stirring the motor, and the temperature uniformity is better.. Each  time 4 groups of samples testing, rotary positioning fixture for each specimen  of impact test and laboratory examination appear brittle failure of minimum  temperature.

新款塑料低溫脆化試驗機測試標準：  

Standard for testing of  multi - functional plastic cryogenic Embrittlement Testing Machine:

GB/T5470-2008塑料沖擊法脆化溫度的測定  

Determination of  embrittlement temperature of plastic impact method

GB/T  12584-2008橡膠或塑料涂覆織物低溫沖擊試驗  

Low temperature impact  test for rubber or plastic coated fabrics

GB/T15256-1994硫化橡膠低溫脆性的測定（多試樣法）  

Determination of low  temperature brittleness of vulcanized rubber (Multi - specimen method)4  

ISO 812-2011硫化橡膠或熱塑性橡膠--低溫脆性的測定  

Vulcanized or  thermoplastic - Determination of low temperature brittleness

BS 903 A25:1992  橡膠的物理試驗.第A25部分:低溫脆性測定  

Physical tests for rubber  - Determination of low temperature brittleness for part A25

ISO 974-2000塑料.沖擊脆化溫度的測定  

Plastics. Determination of  impact embrittlement temperature

ASTM  D2137-2010撓性聚合物及其涂覆織物脆化點測試方法  

Test method for brittle  point of flexible polymer and its coated fabric

ASTM D746-2013用沖擊法測定塑料及彈性材料脆化溫度的試驗方法  

Test method for brittle  temperature of plastic and elastomeric materials by impact method

JIS K7216塑料低溫脆化測試方法  

Test method for low  temperature embrittlement of plastics

JIS K6261-2006硫化或熱塑性橡膠--低溫特性的測定  

Vulcanized or  thermoplastic - Determination of low temperature properties

JIS C3005-2000橡膠或塑料緣電線和電纜的試驗方法  

Test method for rubber or  plastics insulated wires and cable

JIS K  6723-1995增塑聚氯乙烯化合物 Polyvinyl  chloride compound

本標準規定了測定橡膠材料在規定條件下經受沖擊時不出現脆性破壞的溫度或部分試樣出現脆性破壞溫度的方法。 
　　本標準適用于硫化橡膠或熱塑性橡膠低溫脆性的測定。 
　　因為材料的脆性溫度受測試條件和沖擊速度的影響，這樣測得的脆性溫度不是這種材料可以使用的溫度。這種方法獲得的數據只有在變形條件和試驗規定的條件相似的情況下，才可用于預見橡膠材料在低溫下的特性。 
　　描述了三種程序：程序A：測定脆性溫度；程序B：測定50%破壞的脆性溫度；程序C：在規定溫度下沖擊試樣。 
　　程序C用于橡膠材料的分類及評價橡膠材料合性。（對于橡膠涂層織物的類似測試見ISO 4646，橡膠或塑料涂層織物低溫沖擊試驗）

脆性溫度：

在規定條件下一組試樣不產生破壞的溫度。

50%脆性溫度：

在規定的條件下一組試樣50%發生破壞的溫度

試驗速度：

試樣裝置的沖擊頭與被夾緊試樣之間沖擊時的相對線速度（試驗裝置可用于滿足本標準要求的旋轉電機、電磁線圈、重錘、彈簧驅動的沖擊器。標準上只給出電磁線圈低溫沖擊試驗機的速度校準，而我公司是采用伺服電機控制沖擊速度，所以校準伺服電機的轉速即可）

●新款塑料低溫脆化試驗機技術參數：Low  temperature embrittlement testing machine technical parameters - multi  functional plastics